Ivoclar Vivadent Telio Stains - Manual (Page 2)

Interactions
Phenolic substances (e.g. eugenol) may inhibit polymerization.
These materials must not be used in conjunction with Telio
Stains.
Usage
Telio Stains are used in conjunction with Telio CS C&B, Telio
CAD, Telio Lab and Telio Lab LC materials. The temporary
restorations are fabricated according to the corresponding
Instructions for Use.
Application in the dental practice
• Individualization of Telio CS C&B with Telio Stains
Before Telio Stains are applied, carefully blast the surfaces
(using Al
2
O
3
, 100 µm, at 1–2 bar/15–29 psi) or roughen with
coarse diamond burs. Thoroughly rinse with water and dry
with oil-free compressed air. Then wet the areas to be
bonded to extra-orally with Telio Activator. Brush Telio
Activator into the entire surface for at least 30 seconds using
an application brush in order to ensure an even distribution
and quick penetration of Telio Activator. Subsequently, allow
the Activator to react for another 30-60 seconds (total
reaction time 1–2 minutes). Now apply the Heliobond bon-
ding agent, thinly disperse it with blown air and polymerize
for 10 seconds (650 mW/cm
2 , e.g. bluephase using LOP).
Apply the Stains in very thin layers of max. 0.2 mm with a
brush or other suitable instrument (e.g. thin probe). The sha-
de intensity may be reduced and the consistency thinned by
mixing the stains with Heliobond. Finally, polymerize the
stains in accordance with the table below. Apply a suitable
varnish for temporaries according to the instructions of the
manufacturer.
• Polymerization times
Application in the dental laboratory
• Individualization of Telio CAD/Telio Lab with
Telio Stains
Reduce the restorations made of Telio CAD or Telio Lab in
the desired areas according to the principles of the cut-back
technique using cross-cut burs. Check the reduction (cut-
back) with the silicone key. Carefully blast the ground surfa-
ces ( Al
2
O
3
, 100 µm, 1–2 bar/15–29 psi). Then clean with
steam and dry with oil-free compressed air.
Distribute Telio Activator evenly and generously on the con-
ditioned surface and allow it to react for at least 2 minutes
to a maximum of 4 minutes.
Apply SR Composiv to the activated surface according to the
respective Instructions for Use and polymerize.
After that, the conditioned areas can be individualized with
Telio Stains. Apply Telio Stains in very thin layers of max.
0.2 mm with a brush or other suitable instrument or directly
from the thin metal cannula supplied. Final polymerization is
carried out in a light-polymerization device (see polymeriza-
tion table).
• Polymerization times for Telio Stains
The respective light-curing Telio components are pre-
polymerized to ensure that they stay in place and to be able
to apply a further layer. However, final polymerization of the
entire restoration is always required.
After polymerization, cover the Telio Stains with a layer of
Telio Lab or Telio Lab LC Transpa Incisal materials. For more
detailed information, please refer to the Telio Labside
Instructions for Use.
Important
Telio Stains should have room temperature during processing so
that a smooth consistency is ensured. Do not expose Telio
Polymeriza- Manufacturer Output Polymeriza-
tion device mW/cm 2 tion time
bluephase C8 Ivoclar Vivadent 800 mW/cm 2 15 s
bluephase Ivoclar Vivadent 1200 mW/cm 2 10 s
bluephase 20i Ivoclar Vivadent 2000 mW/cm 2 5 s
Polymeriza- Manu- Pre- Final
tion device facturer polimerization polimerization
Quick Ivoclar 40 s ––
Vivadent (SR Composiv
60 s)
Lumamat ® 100 Ivoclar Exclusively use 11 min
(Targis Power Vivadent Quick for pre- (program P2)
Upgrade) polimerization
Spectramat ® Ivoclar 5 min (Telio Stains 5 min
Vivadent (2.5 min)
Visio Beta 1 3M ESPE 7 min, of which 15 min with
10 s vacuum vacuum (pro-
(program depends gram depends
on type of device) on type of device
UniXS 1 Heraeus 90 s 2x 180 s
Solidilite EX 1 Shofu 1 min 5 min