HMC Electronics 40640 Loctite 406 Prism Instant Adhesive, Surface Insensitive, Wicking Grade User Manual

Page 2

background image

TDS LOCTITE

®

406™, November

-

2010

Zinc dichromate

N/mm² 6 to 14

(psi) (870 to 2,030)

ABS

N/mm² 4 to 6

(psi) (580 to 870)

PVC

N/mm² 4 to 6

(psi) (580 to 870)

Polycarbonate

N/mm² 3.5 to 4.5

(psi) (510 to 650)

Phenolic

N/mm² 5 to 15

(psi) (725 to 2,175)

Neoprene

N/mm² 5 to 15

(psi) (725 to 2,175)

Nitrile

N/mm² 5 to 15

(psi) (725 to 2,175)

Tensile Strength, ISO 6922:

Steel (grit blasted)

N/mm² 12 to 25

(psi) (1,740 to 3,625)

Buna-N

N/mm² 5 to 15

(psi) (725 to 2,175)

After 10 seconds @ 22 °C

Tensile Strength, ISO 6922:

Buna-N

N/mm² ≥6.9

LMS

(psi) (≥1,000)

TYPICAL ENVIRONMENTAL RESISTANCE

Cured for 1 week @ 22 °C

Lap Shear Strength, ISO 4587:

Mild Steel (grit blasted)

Hot Strength

Tested at temperature

% Strength @ 22 °C

Temperature, °C

100

75

50

25

0

0

50

100

150

Heat Aging

Aged at temperature indicated and tested @ 22 °C

% Initial Strength @ 22 °C

Exposure Time, hours

125

100

75

50

25

0

0

1000

2000

3000

4000

5000

80 °C

100 °C

60°C

Chemical/Solvent Resistance

Aged under conditions indicated and tested @ 22 °C.

% of initial strength

Environment

°C

100 h

500 h

1000 h

Motor oil (MIL-L-46152)

40

100

100

95

Gasoline

22

100

100

100

Water/glycol 50/50

22

100

100

100

Ethanol

22

100

100

100

Isopropanol

22

100

100

100

Freon TA

22

100

100

100

Heat/humidity 95% RH

40

80

75

65

Heat/humidity 95% RH

on polycarbonate

40

100

100

100

GENERAL INFORMATION
This product is not recommended for use in pure oxygen

and/or oxygen rich systems and should not be selected as

a sealant for chlorine or other strong oxidizing materials

For safe handling information on this product, consult the

Material Safety Data Sheet (MSDS).

Directions for use:

1. For best performance bond surfaces should be clean and

free from grease.

2. This product performs best in thin bond gaps (0.05 mm).
3. Excess adhesive can be dissolved with Loctite cleanup

solvents, nitromethane or acetone.

Loctite Material Specification

LMS

LMS dated May

-

16, 2003. Test reports for each batch are

available for the indicated properties. LMS test reports include

selected QC test parameters considered appropriate to

specifications for customer use. Additionally, comprehensive

controls are in place to assure product quality and

consistency. Special customer specification requirements may

be coordinated through Henkel Quality.

Storage

Store product in the unopened container in a dry location.

Storage information may be indicated on the product container

labeling.

Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or

greater than 8 °C can adversely affect product properties.

Material removed from containers may be contaminated during

use. Do not return product to the original container. Henkel

Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than

those previously indicated. If additional information is required,

please contact your local Technical Service Center or

Customer Service Representative.

Conversions

(°C x 1.8) + 32 = °F

kV/mm x 25.4 = V/mil

mm / 25.4 = inches

µm / 25.4 = mil

N x 0.225 = lb

N/mm x 5.71 = lb/in

N/mm² x 145 = psi

MPa x 145 = psi

N·m x 8.851 = lb·in

N·m x 0.738 = lb·ft

N·mm x 0.142 = oz·in

mPa·s = cP

Henkel Americas

+860.571.5100

Henkel Europe

+49.89.320800.1800

Henkel Asia Pacific

+86.21.2891.8863

For the most direct access to local sales and technical support visit: www.henkel.com/industrial