HMC Electronics 42050 Loctite 420 SuperBonder, Super Bonder Instant Adhesive, Wicking Type Plastic Bonder User Manual

Page 2

background image

TDS LOCTITE

®

420™, January

-

2010

TYPICAL PROPERTIES OF CURED MATERIAL

After 24 hours @ 22 °C

Physical Properties:

Coefficient of Thermal Expansion,

ISO 11359-2, K

-1

100×10

-6

Coefficient of Thermal Conductivity, ISO 8302,

W/(m·K)

0.1

Softening Point, DIN EN 1427, °C

165

Electrical Properties:

Dielectric Constant / Dissipation Factor, IEC 60250:

0.1

-

kHz

2 to 3.3 / <0.02

1

-

kHz

2 to 3.5 / <0.02

10

-

kHz

2 to 3.5 / <0.02

Volume Resistivity, IEC 60093, Ω·cm

2×10

15

to 10×10

15

Surface Resistivity, IEC 60093, Ω

10×10

15

to 80×10

15

Dielectric Breakdown Strength,

IEC 60243-1, kV/mm

25

TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

After 24 hours @ 22 °C

Lap Shear Strength, ISO 4587:

Steel (grit blasted)

N/mm² 15 to 26

(psi) (2,175 to 3,770)

Aluminum (grit blasted)

N/mm² 12 to 19

(psi) (1,740 to 2,755)

Zinc dichromate

N/mm² 6 to 13

(psi) (870 to 1,885)

ABS

N/mm² 6 to 20

(psi) (870 to 2,900)

PVC

N/mm² 6 to 20

(psi) (870 to 2,900)

Polycarbonate

N/mm² 6 to 20

(psi) (870 to 2,900)

Phenolic

N/mm² 5 to 20

(psi) (725 to 2,900)

Neoprene

N/mm² 5 to 15

(psi) (725 to 2,175)

Nitrile

N/mm² 5 to 15

(psi) (725 to 2,175)

Tensile Strength, ISO 6922:

Steel

N/mm² 12 to 25

(psi) (1,740 to 3,625)

Buna-N

N/mm² 5 to 15

(psi) (725 to 2,175)

"T" Peel Strength, ISO 11339:

Steel (degreased)

N/mm <0.5

(lb/in) (<2.8)

After 10 seconds @ 22 °C

Tensile Strength, ISO 6922:

Buna-N

N/mm² ≥6.0

LMS

(psi) (≥870)

TYPICAL ENVIRONMENTAL RESISTANCE

Cured for 1 week @ 22 °C

Lap Shear Strength, ISO 4587:

Mild Steel (grit blasted)

Hot Strength

Tested at temperature

% Strength @ 22 °C

Temperature, °C

100

75

50

25

0

-50

0

50

100

150

Heat Aging

Aged at temperature indicated and tested @ 22 °C

% Initial Strength @ 22 °C

Exposure Time, hours

100

75

50

25

0

0

1000

2000

3000

4000

5000

60°C

80°C

100°C

Chemical/Solvent Resistance

Aged under conditions indicated and tested @ 22 °C.

% of initial strength

Environment

°C

100 h

500 h

1000 h

Motor oil (MIL-L-46152)

40

100

100

95

Gasoline

22

100

100

100

Isopropanol

22

100

100

100

Ethanol

22

100

100

100

Freon TA

22

100

100

100

1,1,1 Trichloroethane

22

100

100

100

Heat/humidity 95% RH

40

80

75

65

Heat/humidity 95% RH

on polycarbonate

40

100

100

100

GENERAL INFORMATION
This product is not recommended for use in pure oxygen

and/or oxygen rich systems and should not be selected as

a sealant for chlorine or other strong oxidizing materials

For safe handling information on this product, consult the

Material Safety Data Sheet (MSDS).

Directions for use:

1. For best performance bond surfaces should be clean and

free from grease.

2. This product performs best in thin bond gaps (0.05 mm).
3. Excess adhesive can be dissolved with Loctite cleanup

solvents, nitromethane or acetone.

Henkel Americas

+860.571.5100

Henkel Europe

+49.89.320800.1800

Henkel Asia Pacific

+86.21.2891.8863

For the most direct access to local sales and technical support visit: www.henkel.com/industrial

Documentation Provided By HMC Electronics

33 Springdale Ave. Canton, MA 02021

http://www.hmcelectronics.com

(800) 482-4440