TDS LOCTITE

®

660™, December

-

2009

Cure Speed vs. Activator

Where cure speed is unacceptably long, or large gaps are

present, applying activator to the surface will improve cure

speed. The graph below shows the shear strength developed

with time on zinc dichromate steel pins and collars using

Activator 7471™ and 7649™ and tested according to ISO

10123.

% of Full Strength on Steel

Cure Time

100

75

50

25

0

1min

5min10min 30min 1h

3h 6h

24h

72h

Activator 7471™

Activator 7649™

No activator

TYPICAL PROPERTIES OF CURED MATERIAL

Physical Properties:

Coefficient of Thermal Expansion,

ISO 11359-2, K

-1

80×10

-6

Coefficient of Thermal Conductivity, ISO 8302,

W/(m·K)

0.1

Specific Heat, kJ/(kg·K)

0.3

Elongation, at break, ISO 37, %

<2

TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars

N/mm² ≥17.2

LMS

(psi) (2,490)

TYPICAL ENVIRONMENTAL RESISTANCE

Cured for 1 week @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars

Hot Strength

Tested at temperature

% Strength @ 22 °C

Temperature, °C

100

75

50

25

0

-50

0

50

100

150

Heat Aging

Aged at temperature indicated and tested @ 22 °C

% Initial Strength @ 22 °C

Exposure Time, hours

200

150

100

50

0

0

1000

2000

3000

4000

5000

120 °C

150 °C

Chemical/Solvent Resistance

Aged under conditions indicated and tested @ 22 °C.

% of initial strength

Environment

°C

100 h

500 h

1000 h

Motor oil (MIL-L-46152)

125

100

100

100

Unleaded gasoline

22

100

100

100

Brake fluid

22

80

75

75

Water/glycol 50/50

87

100

90

80

Ethanol

22

95

95

95

Acetone

22

80

80

80

GENERAL INFORMATION
This product is not recommended for use in pure oxygen

and/or oxygen rich systems and should not be selected as

a sealant for chlorine or other strong oxidizing materials

For safe handling information on this product, consult the

Material Safety Data Sheet (MSDS).

Where aqueous washing systems are used to clean the

surfaces before bonding, it is important to check for

compatibility of the washing solution with the adhesive. In

some cases these aqueous washes can affect the cure and

performance of the adhesive.

This product is not normally recommended for use on plastics

(particularly thermoplastic materials where stress cracking of

the plastic could result). Users are recommended to confirm

compatibility of the product with such substrates.

Directions for use:
For Assembly

1. For best results, clean all surfaces (external and internal)

with a LOCTITE

®

cleaning solvent and allow to dry.

2. If the material is an inactive metal or the cure speed is too

slow, spray with Activator 7471™ or 7649™ and allow to

dry.

3. For Slip Fitted Assemblies, apply adhesive around the

leading edge of the pin and the inside of the collar and

use a rotating motion during assembly to ensure good

coverage.

4. For Press Fitted Assemblies, apply adhesive thoroughly

to both bond surfaces and assemble at high press on

rates.

Henkel Americas

+860.571.5100

Henkel Europe

+49.89.320800.1800

Henkel Asia Pacific

+86.21.2891.8863

For the most direct access to local sales and technical support visit: www.henkel.com/industrial

Documentation Provided By HMC Electronics

33 Springdale Ave. Canton, MA 02021

http://www.hmcelectronics.com

(800) 482-4440