Ivoclar Vivadent Telio Lab - Manual (Page 14)

Important
A higher room temperature shortens the processing time. The mixing ratio between the
polymer and the monomer also influences the processing time. If the mixing ratio is correctly
observed, a relatively flowable consistency is achieved.
Preparing and isolating the model
– Remove the silicone key from the model once it is set and clean off any wax residue from the model.
– Block out undercuts and cuts between model segments.
– Immerse the model in water for 5 minutes. Then, apply two layers of Separating Fluid. Wait between
the two layers until the surface is no longer shiny.
Powder/liquid mixing ratio
– Pour the desired amount of Telio Lab Cold Liquid into a clear mixing beaker.
– Dispense the same amount of powder into a second mixing beaker.
– Subsequently, add the powder to the Cold Liquid and mix without creating air bubbles using a model-
ling spatula.
– Cover the beaker and allow a dough time of approximately 2 minutes.
– Pour the now well-flowable Telio Lab resin evenly into the silicone key.
– Once the resin has reached its plastic phase, it can be contoured using an instrument that has been
wetted with monomer.
Information
Rough surfaces or undercuts may be isolated or blocked out using the elastic isolating gel
SR Ivocron
® . Apply SR Ivocron Separator and allow to dry for approximately 5 minutes.
Volume mixing
ratio Weight mixing
ratio
Mixing time Dough time Casting phase Plastic
phase
1 part polymer :
1 part monomer
1 g polymer :
0.83 g monomer
20 s 2 min 2 min 3 min 15 min
Processing time at 23 °C/73 °F approximately 8 minutes
Mixing ratio 1:1 2 minutes dough time
Polymerization in
the pressure pot
2-6 bar/29-87 psi,
40-50°C/104–122°F
14