Ivoclar Vivadent IPS e.max Ceram User Manual
Page 69
69
Depending on the furnace type, the firing temperature can be reduced by 5 °C to max. 10 °C (9 °F to max. 18 °F) for the
2
nd
Dentin / Incisal firing.
Firing of zirconium oxide (ZrO
2
)--supported restorations
– Several units (e.g. multi-unit bridges with bulky pontics) in the furnace impede even and thorough heating of the
individual units.
– Heat penetration in the firing chamber depends on the type of furnace and the size of the firing chamber.
– The parameters listed in the Instructions for Use apply to Ivoclar Vivadent furnaces (temperature tolerance ± 10 ºC/18 °F).
– If furnaces other than those from Ivoclar Vivadent are used, temperature adjustments may be necessary.
– At the beginning, open the furnace and wait for the acoustic signal. Subsequently, place the firing tray with the objects
in the center of the firing table and start the program.
– Remove IPS e.max objects from the furnace after completion of the firing cycle (wait for the acoustic signal of the
furnace).
– Allow the objects to cool to room temperature in a place protected from draft.
– Do not touch the hot objects with metal tongs.
– Do not blast or quench the objects.
IPS e.max Ceram on IPS e.max ZirPress (Staining technique)
IPS e.max Ceram on IPS e.max ZirPress (Cut-back and Layering technique)
IPS e.max Ceram on IPS e.max ZirPress
B
S
t
➚
T
H
V
1
V
2
L
Staining Technique
°C/°F
min
°C/°F//min
°C/°F
min
°C/°F
°C/°F
°C/°F
ZirLiner firing – before wax-up and pressing
403/757
4:00
40/72
960/1760
1:00
450/842
959/1758
Stain and characterization firing
403/757
6:00
60/108
770/1418 1:00-2:00
450/842
769
450/842
Glaze firing
403/757
6:00
60/108
770/1418 1:00-2:00
450/842
769
450/842
Add-On after Glaze firing
403/757
6:00
50/90
700/1292
1:00
450/842
699
450/842
IPS e.max Ceram on IPS e.max ZirPress
B
S
t
➚
T
H
V
1
V
2
L
Cut-back and Layering technique
°C/°F
min
°C/°F/min
°C/°F
min
°C/°F
°C/°F
°C/°F
ZirLiner firng – before wax-up and pressing
403/757
4:00
40/72
960/1760
1:00
450/842
959/1758
Wash firing (Foundation)
403/757
4:00
40/72
750/1382
1:00
450/842
749/1380
Wash firing (Foundation) characterization
403/757
4:00
40/72
750/1382
1:00
450/842
749/1380
1
st
Dentin/Incisal firing
403/757
4:00
40/72
750/1382
1:00
450/842
749/1380
2
nd
Dentin/Incisal firing
403/757
4:00
40/72
750/1382
1:00
450/842
749/1380
Stain firing
403/757
6:00
60/108
725/1337
1:00
450/842
724/1335
450/842
Glaze firing
403/757
6:00
60/108
725/1337
1:00
450/842
724/1335
450/842
Add-On with Glaze firing
403/757
6:00
60/108
725/1337
1:00
450/842
724/1335
450/842
Add-On after Glaze firing
403/757
6:00
50/90
700/1292
1:00
450/842
699/1290
450/842