– Two-component core build-up material
– Zweikomponenten Stumpfaufbaumaterial
– Matériau de reconstitution de faux-moignons
– Composito bicomponente per la ricostruzione del moncone
– Material de muñones bicomponente
– Material bi-componente para confecção de núcleos
– Tvåkomponents pelaruppbyggnadsmaterial
– To-komponent plastopbygningsmateriale
– Kaksikomponenttinen pilarimateriaali
– Tokomponent konusoppbyggingsmateriale
– Tweecomponenten-stompopbouwmateriaal
– Yλικ ανασύστασης κολοβωµάτων δύο συστατικών
– ‹ki bileflenli core inflası malzemesi
– Ñ‚ÛıÍÓÏÔÓÌÂÌÚÌ˚È Ï‡ÚÂˇΠ‰Îfl ‚ÓÒÒÚ‡ÌÓ‚ÎÂÌËfl ÍÛθÚË
– Dwuskładnikowy materiał do wykonywania
podbudowy pod uzupełnienia protetyczne
Description
MultiCore is a dual-curing, radiopaque composite containing fluoride fillers
that demonstrates excellent mechanical properties for core build-ups. It
cures chemically without the use of light. Light-curing is optional.
MultiCore is available in two different viscosities:
– MultiCore Flow in a double-barrel cartridge or a double-push syringe
with automixing tips for fabricating core build-ups using matrices
– MultiCore HB in two syringes (base and catalyst paste) for hand-mixing
suitable for individually moulded composite cores.
Composition
MultiCore Flow
The monomer matrix consists of dimethacrylate (29 wt %).
The inorganic fillers are barium glass, ytterbiumtrifluoride, Ba-Al-fluorosili-
cate glass and highly dispersed silicon dioxide (70 wt %).
Additional contents are catalysts, stabilizers and pigments (1 wt %).
The total content of inorganic fillers is 46 vol %. The particle size ranges
from 0.04 to 25 µm.
MultiCore HB
The monomer matrix consists of dimethacrylate (13.5 wt %). The inorganic
fillers are barium glass, ytterbiumtrifluoride, Ba-Al-fluorosilicate glass and
highly dispersed silicon dioxide (86 wt %). Additional contents are catalysts,
stabilizers and pigments (0.5 wt %). The total contents of inorganic fillers is
70 vol %. Particle sizes range from 0.04 to 25 µm.
Shades
MultiCore is available in four shades:
The dentin shades light (A1/B1), medium (A2/A3) and white-opaque are
particularly suitable for use under all-ceramic restorations, and blue is
recommended for use under metal or metal-based veneered crowns.
Working time
MultiCore Flow:
90 to 120 s (at 37°C/98.6°F)
MultiCore HB: 90 to 120 s (at 37°C/98.6°F)
or 120 to 150 s (at room temperature)
Mixing ratio
The base and catalyst pastes of MultiCore are mixed at a ratio of 1:1. Multi-
Core Flow is mixed by pressing the pastes through the static mixing tip. The
MultiCore HB pastes should be mixed on the mixing pad included in the
package with the accompanying spatula.
Indications
– Core build-up of vital and non-vital teeth.
– Adhesive cementation of glass fibre-reinforced endodontic posts
579328/0411/G
English