USG SHEETROCK Wall and Ceiling Spray Texture Unaggregated User Manual
Wall and ceiling spray texture, Unaggregated, Heetrock
Surface
Substrate must be sound, dry, clean, and free of oil, grease, mildew, efflorescence, and other foreign materials
Preparation
and/or contaminants. Product, air, and surface temperatures must be maintained at a minimum of 55 °F (13 °C)
throughout the finishing process when using joint compound, primer, and texture products.
New Drywall
Treat joints and nailheads with an appropriate USG Joint Treatment System.
New Concrete/Plaster
Age at least 60 days before texturing. Remove form oils and efflorescence and grind down
form lines. Fill cracks and holes, and level concrete surfaces with S
HEETROCK
®
Brand D
URABOND
®
Setting-Type or
E
ASY
S
AND
™
Lightweight Setting-Type Joint Compound or Cover Coat
®
Brand Compound and let dry.
Substrate
Application of a prime coat is necessary to equalize surface porosity. After prepared surfaces have thoroughly
Priming
dried, apply a prime coat of S
HEETROCK
®
Brand First Coat flat latex paint or a good quality interior latex flat wall
paint with high solids content. Prime coat should be applied undiluted and allowed to dry before decorating.
Mixing
Use a clean vessel equipped with power agitator. For initial mix, stir powder into recommended amount of water,
agitating during powder addition. Allow to soak for at least 15 min.—longer in cold water. Remix until a creamy,
lump-free mix is obtained. Adjust spray consistency by adding small amounts of powder or water. Overthinning
can create an undesirable finish or “soft wall” or chalky condition. Overdilution can also entrain excessive air
and foam.
Application
Using suitable spray equipment, apply by machine to create the desired effect. The application rate will vary
from 10 ft.
2
/lb. (2 m
2
/kg) to 40 ft.
2
/lb. (8.2 m
2
/kg) depending on texture pattern. Maintain 55 °F (13 °C) minimal
air, product, and surface temperature during application and until surface is dry. Avoid drafts while applying, but
provide ventilation after application to aid drying. Do not use unvented gas or oil heaters. May be painted after
overnight drying. Unpainted surface is not washable or scrubbable. Match spray equipment to job size and time
requirements. For rapid application and high production, use either a piston pump (7:1 or larger) or a rotor sta-
tor pump matched to a compressor of adequate size. Preferred texture patterns can be obtained using a Binks
18D spray gun (with #57 or 58 fluid nozzle with R27 or R30 fan cap) or Binks 7E2 spray gun (with #46 fluid
nozzle with #190, 191, 290, 291, or 292 fan cap). Fan caps with a rectangular orifice reduce overspray and
waste and will provide greater spray control. Good results can also be obtained using a short pole gun with a
3/8
Љ nozzle orifice. Small jobs can be completed using a Hopper Gun or Goldblatt Pattern Pistol with separate
compressor.
S
HEETROCK
®
Brand
Wall and Ceiling Spray Texture
Application Tips
Unaggregated
Manufactured by
United States Gypsum Company
125 South Franklin Street
Chicago, IL 60606
800 USG.4YOU (874-4968)
www.usg.com
J1824/2-04
©2004, United States Gypsum Company
Printed in U.S.A.
Trademarks
The following trademarks used
herein are owned by United
States Gypsum Company or a
related company: C
OVER
C
OAT
,
D
URABOND
, E
ASY
S
AND
, S
HEETROCK
.
Note
Products described here may
not be available in all geographic
markets. Consult your U.S.
Gypsum Company sales office
or representative for information.
Notice
We shall not be liable for inci-
dental or consequential dam-
ages, directly or indirectly sus-
tained, nor for any loss caused
by application of these goods
not in accordance with current
printed instructions or for other
than their intended use. Our lia-
bility is expressly limited to
replacement of defective goods.
Any claim shall be deemed
waived unless made in writing
to us within thirty (30) days from
the date it was or reasonably
should have been discovered.
SAFETY FIRST!
Follow good safety practices.
Read material safety data
sheets and related literature on
products before specification
and/or installation.