Ivoclar Vivadent IPS e.max Clinical Guide - Manual (Page 19)

19
Practical procedure for restorations with IPS e.max | Cementation
Intraoral adjustments
Recommended grinding instruments for ceramics – use in the dental office
To achieve the expected clinical properties of the ceramic materials, exact polishing after adjustments by grinding
is imperative.
Layering ceramics /
Schichtkeramik
Flexural strength /
Biegefestigkeit
80–130 MPa
Type of ceramic /
Keramiktyp
Extensive corrections /
Grosse Korrekturen
Minor corrections /
Geringe Korrekturen
Endo Access Polishing / Politur
(OptraFine)
extra fine /
extra fein
15–25 µm
extra fine /
extra fein
15–25 µm
medium
<_100 µm
extra fine /
extra fein
15–25 µm
extra fine /
extra fein
15–25 µm
medium
<_100 µm
fine / fein
40–50 µm
extra fine /
extra fein
15–25 µm
medium
<_100 µm
fine / fein
40–50 µm
fine / fein
40–50 µm
medium
<_100 µm
Leucite-reinforced glass-ceramic /
Leuzitverstärkte Glasskeramik
Flexural strength /
Biegefestigkeit
160 MPa
Lithium disilicate glass-ceramic /
Lithiumdisilikat-Glaskeramik
Flexural strength /
Biegefestigkeit
360–400 MPa
Zirconium oxide / Zirkoniumoxid
Flexural strength /
Biegefestigkeit
900 MPa
d.SIGN IPS ® InLine PoM ® IPS
InLine ® IPS
Empress IPS ®
Esthetic
Empress IPS ®
CAD
before polishing /
vor der Politur
Finisher F Polisher P High gloss
+ Polishing Paste
after polishing /
nach der Politur
before polishing /
vor der Politur
Finisher F Polisher P High gloss
+ Polishing Paste
after polishing /
nach der Politur
before polishing /
vor der Politur
Finisher F Polisher P High gloss
+ Polishing Paste
after polishing /
nach der Politur
IPS
e.max
IPS
InLine/IPS
InLine
PoM
IPS
d.SIGN
Recommended grinding instruments for ceramics – use in the dental practice
Schleifkörperempfehlung für Keramik – Anwendung in der zahnärztlichen Praxis
The provided grain sizes of the diamond burs are recommendations for ceramic materials from Ivoclar Vivadent.
The corresponding directions of the manufacturer of the grinding instruments regarding their correct use, e.g.
speed, have to be observed.