3. Disperse AdheSE Bond / Heliobond with a very weak stream of air.
Avoid pooling! Care should be taken not to blow away the bonding
agent. All the prepared surfaces must be adequately coated with
AdheSE Bond.
Note: AdheSE Bond / Heliobond does not contain a solvent that needs
to be evaporated!
4. Polymerize AdheSE Bond / Heliobond for 10 s using a LED or halogen
curing light with a light intensity of more than 500 mW/cm 2 (eg
bluephase in the LOW mode). If other curing lights are used (eg plasma
arc or laser curing units), the recommendations of the respective manu-
facturer must be followed to obtain fully polymerized results. The
curing time depends on the intensity and the wavelength range of the
light emitted by the different curing units. Curing times of less than 5 s
are not recommended.
5. Apply Telio CS C&B
6. If necessary, finish the relined, repaired and adjusted areas of the Telio
CS C&B temporary with eg cross-cut tungsten carbide burs and subse-
quently polish them with silicon carbide rubber polishers (eg OptraPol
® ).
Alternatively, Telio CS C&B temporaries can be repaired or adjusted directly
with a light-curing Ivoclar Vivadent composite (eg Telio Add-On Flow, Tetric
EvoFlow
® ). In this case, the respective Instructions for Use or Telio Chair-
side Instructions of Use must be observed.
If Telio CS C&B, Telio CAD and/or Telio Lab restorations are repaired, relined
or adjusted at a later date, the respective Telio Chairside / Telio Labside
Instructions for Use must be observed.
Working time
Approx. 1 minute at room temperature (23°C / 73°F).
Setting time
Approx. 1 to 2 minutes at 37 °C / 98 °F, approx. 3 minutes at room
temperature (23 °C / 73 °F).
Special notes
– Uncured material can be removed using alcohol or similar solvents.
– Alternatively to extruding and discarding a pea-sized amount of
material prior to each application, extrude just as much base and cata-
lyst until even strands of both pastes are produced before attaching
the mixing tip.
Precautions
–
Post-retained temporary crowns are only indicated for a short period.
Exposed to higher loads and during longer periods of clinical function
they may cause vertical root fractures. Furthermore, they do not provide
protection against reinfection of the root canal system.
– Prevent any contact of uncured Telio CS C&B with the skin/mucous
membrane and eyes.
– Uncured Telio CS C&B may cause slight irritation and may lead to a
sensitization against methacrylates.
– Commercially available medical gloves do not provide protection
against the sensitizing effect of methacrylates.
Storage and shelf life
–
Shelf life: see expiration date on label
– Storage temperature 2–28 °C / 36–82 °F
– Only use Telio CS C&B at room temperature (cooled material is more
viscous and exhibits a slower setting behaviour).
– Store cartridge in a horizontal position or in the dispenser, do not store
in an upright position.
Keep out of the reach of children!
For use in dentistry only!
Date information prepared: 12/2011, Rev. 3
Manufacturer
Ivoclar Vivadent AG, FL-9494 Schaan/Liechtenstein
The product has been developed solely for use in dentistry. Processing should be carried out strictly
according to the Instructions for Use. Liability cannot be accepted for damages resulting from failure to
observe the Instructions or the stipulated area of application. The user is responsible for testing the
products for their suitability and use for any purpose not explicitly stated in the Instructions. Descrip-
tions and data constitute no warranty of attributes.